Physical properties of chromium-nickel martensitic stainless steel 00Cr13Ni5Mo

Stainless steel 1202 30/06/2023 1063 Aiden

Chemical Composition of 00Cr13Ni5Mo Stainless Steel 00Cr13Ni5Mo stainless steel belongs to Cr13Ni5Mo steel, an austenitic stainless steel with a martensitic transformation. This martensitic transformation is responsible for the excellent magnetism properties of this material. The chemical composi......

Chemical Composition of 00Cr13Ni5Mo Stainless Steel

00Cr13Ni5Mo stainless steel belongs to Cr13Ni5Mo steel, an austenitic stainless steel with a martensitic transformation. This martensitic transformation is responsible for the excellent magnetism properties of this material. The chemical composition of 00Cr13Ni5Mo stainless steel is as follows:

C Si Mn P S Cr Ni Mo 0.05-0.13 ≤0.6 ≤1 ≤0.035 ≤0.03 12.5-15 4.5-5.5 2.5-3.5

Physical Properties of 00Cr13Ni5Mo Stainless Steel

The physical properties of 00Cr13Ni5Mo stainless steel are as follows:

Density: 7.77g/cm3

Specific Heat: 450J/(kg·K)

Thermal Conductivity: 25.2W/(m·K)

Electrical Resistivity: 17.9μΩ·m

Thermal Expansion: 13.4×10-6/K

Mechanical Properties of 00Cr13Ni5Mo Stainless Steel

00Cr13Ni5Mo stainless steel has excellent mechanical properties, such as high strength, hardness and ductility. Its mechanical properties are as follows:

Tensile Strength: ≥520MPa

Yield Strength: ≥535MPa

Elongation: ≥15%

Reduction of Area: ≥10%

Hardness: ≤200HB

Impact Properties of 00Cr13Ni5Mo Stainless Steel

Impact properties of 00Cr13Ni5Mo stainless steel include impact strength, impact resistance, impact toughness and toughness. Its impact properties are as follows:

Impact Strength: ≥400kJ/m2

Impact Resistance: ≥20%

Impact Toughness: ≥40J/cm2

Toughness: ≥500MPa

Applications of 00Cr13Ni5Mo Stainless Steel

00Cr13Ni5Mo stainless steel has a number of applications in various industries, such as chemical and petrochemical, food processing, energy, construction, and medical. This material is excellent for its corrosion resistance, heat resistance, hardness, strength, ductility and wear resistance. It is used in the manufacture of tanks, pipes, valves, structural components and many other industrial items. This material is also used in medical implants.

Put Away Put Away
Expand Expand
Stainless steel 1202 2023-06-30 1063 AuroraLights

00Cr13Ni5Mo stainless steel is a martensite stainless steel in China. It has good mechanical properties, wear resistance and corrosion resistance, and is widely used in petroleum, chemical, food and medical industries. The physical properties of 00Cr13Ni5Mo stainless steel are as follows: 1. Che......

00Cr13Ni5Mo stainless steel is a martensite stainless steel in China. It has good mechanical properties, wear resistance and corrosion resistance, and is widely used in petroleum, chemical, food and medical industries.

The physical properties of 00Cr13Ni5Mo stainless steel are as follows:

1. Chemical composition: C=0.04%, Si=0.69%, Mn=0.33%, P=0.03%, S= =0.03%, Cr=12.8%, Ni=4.4%, Mo=2.4%.

2. Density: 7.75g/cm³

3. Elastic modulus: 192 GPa

4. Ultimate tensile strength: 553 MPa

5. Hardness: HRC=36

6. Yield strength (0.2% offset): 435 MPa

7. Thermal conductivity: 25.080 W/m.K;

8. Electrical conductivity: 8.7×106/m

9. Melting point: 1387-1399℃

00Cr13Ni5Mo stainless steel has good workability and can be used in corrosive and wear-resistant applications due to its high strength, corrosion resistance and wear resistance. It has oxidation resistance and is often used as structural materials in industrial applications. It is non-magnetic and has good weldability, machinability and formability, making it suitable for a variety of manufacturing operations.

In conclusion, 00Cr13Ni5Mo stainless steel, with its excellent physical properties, is a great choice for industrial applications. It is widely used in industries such as petrochemical, medical, food and other industries.

Put Away
Expand

Commenta

Please surf the Internet in a civilized manner, speak rationally and abide by relevant regulations.
Featured Entries
two stage bidding
03/07/2023
low alloy steel
13/06/2023
Malleability
13/06/2023