1Cr19Ni9 heat-resistant steel rod

1Cr19Ni9 Heat Resistant Steel Bar

1Cr19Ni9 is a heat resistant steel bar manufactured by Baosteel Group Corporation, one of the most significant steel bar producers in China. It has an excellent combination of strength and toughness in its properties, making it the perfect choice for highly demanding commercial and industrial applications.

1Cr19Ni9 is made of the best quality iron and combines chromium, nickel, and molybdenum to achieve improved corrosion resistance and extremely high mechanical properties. This steel bar is heat-treated with additional elements to form a protective layer and to enhance its strength and wear resistance. The heat treatment also relieves the brittleness and enables 1Cr19Ni9 to maintain its high workability and toughness.

1Cr19Ni9 is the ideal material for producing springs, bolts, and heavy load-bearing structures. It is usually employed in the manufacture of heavy-duty parts such as crankshafts, valves, and gears. 1Cr19Ni9 is also used to make items such as scaffoldings, pipes, tanks, and containers. The exceptional hardness, toughness, and heat-resistanceAlso make Hbeiyang an excellent material for aerospace components such as landing gear.

1Cr19Ni9 performs exceptionally well in a wide range of temperatures. Its temperature range is usually between 400 and 600 degrees Celsius, although the range may be extended depending on the type of work required of the steel bar. The increased resistance to oxidation and corrosion makes 1Cr19Ni9 the perfect material for both commercial and industrial applications that require a significant amount of strength and durability.

1Cr19Ni9 exceeds industry standards in terms of tensile strength and yield strength, implying that it delivers substantial value for money. Its ductility and shrinkage enable it to be fabricated with ease, making it an advantageous option for engineers and manufacturers alike.

Take advantage of this terrific heat-resistant steel bar from Baosteel by ordering your stock from us today. We ensure Prompt Delivery and provide Comprehensive After-sale Services and Support at all times.

1Cr19Ni9 Heat Resistant Steel Bar

1Cr19Ni9 Heat Resistant steel bar, referred to as heat-resistant steel bar”, belongs to Cr-Ni austenitic heat-resistant stainless steels. It is based on steel grade 1Cr18Ni9 and adds N, Ti and other metal elements to increase its stability and resistance to intercrystalline corrosion.

1Cr19Ni9 Heat Resistant steel bar has good oxidation resistance and increases in service temperature up to 800℃ or so. Its strength, plasticity and corrosion resistance are comparable to 304 stainless steel and is mainly used in the manufacture of gas turbine combustion chamber and related structural components, and mechanical components for Continuous high temperature operation.

1Cr19Ni9 Heat Resistant steel bar usually does not require heat treatment before processing. Generally, after the process and welding, annealing treatment should be taken. After being annealed, the mechanical properties and corrosion resistance of 1Cr19Ni9 Heat Resistant steel bar can be kept stable and meet the requirements. During annealing, the temperature should not be too high, Generally 550-650℃.

1Cr19Ni9 Heat Resistant steel bar has good forming performance and no special precautions are required during forming process. Compared with 1Cr18Ni9Ti, 1Cr19Ni9 Heat Resistant steel bar has a lower resistance to intercrystalline corrosion, so the stress relieved after welding should be as small as possible, and when welding and thermal cutting, insufficient protection should be paid attention to, otherwise porosity and transgranular intergranular cracks are easy to appear. All parts must be stress relieved and annealed after welding. The welding rod should better undergo a water cooling treatment to reduce its hardness.

1Cr19Ni9 Heat Resistant steel bar has good hot and cold processing performance, no embrittlement and better cutting performance. It can be cut by both Oxyacetylene and electric arc burning, and manual arc burning welding is also possible, but the treatment after welding must be strictly controlled.

1Cr19Ni9 heat-resisting steel bar has outstanding corrosion resistance, high strength, outstanding performance and good stability, so it is widely used in many industries.