The chemical composition of 00Cr13Ni5Mo Martensitic Stainless Steel
00Cr13Ni5Mo Martensitic Stainless Steel is a high chromium alloy of stainless steel, which is composed of 13% chromium and 5% nickel. This alloy offers excellent corrosion resistance and good heat resistance, making it a great choice for use in the food industry or in other industrial applications.
Chemical Composition:
00Cr13Ni5Mo Martensitic Stainless Steel is composed of the following chemical elements:
Carbon (C): 0.080 - 0.12%
Manganese (Mn): 0.50%
Silicon (Si): 0.50%
Chromium (Cr): 12.00 - 13.50%
Nickel (Ni): 4.50 - 5.50%
Phosphorus (P): 0.040%
Sulfur (S): 0.030%
Mechanical Properties:
00Cr13Ni5Mo Martensitic Stainless Steel offers excellent mechanical properties, such as high tensile strength and yield strength, good corrosion resistance, and high hardness. Its tensile strength is between 488 and 790MPa, while its yield strength is between 453 and 690MPa. This alloy also offers excellent undergoes weldability, with good machinability, making it a great choice for an array of industrial and food applications.
Applications:
00Cr13Ni5Mo Martensitic Stainless Steel is widely used for food and industrial applications, due to its excellent corrosion and wear resistant properties. This material can be readily machined and welded, making it ideal for use in the food industry for food processing machinery. It can also be used for many industrial applications, such as corrosive containers, pipe supporting structures and machine parts, among others.
Conclusion:
00Cr13Ni5Mo Martensitic Stainless Steel is a high chromium alloy of stainless steel, composed of 13% chromium and 5% nickel. This material offers excellent corrosion resistance, good heat resistance, and high tensile strength and yield strength. It is widely used in food processing machinery and industrial applications, due to its excellent wear and corrosion resistance, as well as its good machinability and weldability.